Liquid-crystalline compounds

ABSTRACT

The invention relates to liquid-crystalline compounds of the formula I,  
                 
 
     and to liquid-crystalline media comprising at least one compound of the formula I and to electro-optical displays containing such a liquid-crystalline medium.

[0001] The present invention relates to liquid-crystalline compounds and to a liquid-crystalline medium, to its use for electro-optical purposes and to displays containing said medium.

[0002] Liquid crystals are used especially as dielectrics in display devices, as the optical properties of such substances can be affected by an applied voltage. Electro-optical devices on the basis of liquid crystals are very well known to those skilled in the art and can be based on various effects. Examples of such devices include cells with dynamic scattering, DAP cells (deformation of aligned phases), guest/host cells, TN cells having a twisted nematic structure, STN cells (supertwisted nematic), SBE cells (superbirefringence effect) and OMI cells (optical mode interference). The most common display devices are based on the Schadt-Helfrich effect and have a twisted nematic structure.

[0003] The liquid crystal materials must have good chemical and thermal stability and good stability with respect to electrical fields and electromagnetic radiation. Additionally, the liquid crystal materials should have a low viscosity and give rise to short response times, low threshold voltages and high contrast in cells.

[0004] Furthermore they should, at standard operating temperatures, i.e., in as wide a range as possible below and above room temperature, have a suitable mesophase, for example a nematic or cholesteric mesophase for the abovementioned cells. Since liquid crystals as a rule are used as mixtures of a number of components, it is important for the components to be readily miscible with one another. Other properties such as electrical conductivity, dielectric anisotropy and optical anisotropy must meet various requirements, depending on the cell type and field of application. For example, materials for cells having a twisted nematic structure should exhibit positive dielectric anisotropy and low electrical conductivity.

[0005] Matrix liquid crystal displays, for example, comprising integrated nonlinear elements to switch individual pixels (matrix LCDs) ideally require media having large positive dielectric anisotropy, broad-range nematic phases, relatively low birefringence, very high resistivity, good UV and temperature stability and low vapor pressure.

[0006] Such matrix liquid crystal displays are known. Suitable nonlinear elements for individually switching the separate pixels include active elements (i.e. transistors), for example. Such an arrangement is referred to as an “active matrix”, allowing for a distinction between two types:

[0007] 1. MOS (metal oxide semiconductor) or other diodes on a silicon wafer as the substrate.

[0008] 2. Thin-film transistors (TFT) on a glass sheet as the substrate.

[0009] The use of monocrystalline silicon as a substrate material limits the display size, since even modular assembly of separate subdisplays gives rise to problems at the joints.

[0010] In the more promising type 2, which is preferred, the electro-optical effect used is usually the TN effect. A distinction is made between two technologies: TFTs composed of compound semiconductors such as CdSe, or TFTs on the basis of polycrystalline or amorphous silicon. Work on the latter technology is being carried out worldwide with great intensity.

[0011] The TFT matrix is applied on the inside of the one glass sheet of the display, while the other glass sheet on its inside carries the transparent counter-electrode. Compared with the size of the pixel electrode, the TFT is very small and hardly interferes with the image. This technology can also be extended to full color capability pictorial representations, where a mosaic of red, green and blue filters is arranged in such a way that filter elements are located opposite switchable picture elements in a one-to-one arrangement.

[0012] The TFT displays usually function as TN cells comprising crossed polarizers in transmission and employ backlighting.

[0013] The term matrix LCDs in this context encompasses any matrix display comprising integrated nonlinear elements, i.e. in addition to the active matrix it also includes displays comprising passive elements such as varistors or diodes (MIM=metal-insulator-metal).

[0014] Matrix LCDs of this type are suitable, in particular, for TV applications (e.g. portable televisions) or for high information level displays for computer applications (laptop) and in motor vehicle or aircraft production. In addition to problems regarding angular dependence of contrast and switching times, matrix LCDs present difficulties owing to insufficiently high resistivity of the liquid crystal mixtures [TOGASHI, S., SEKIGUCHI, K., TANABE, H., YAMAMOTO, E., SORIMACHI, K., TAJIMA, E., WATANABE, H., SHIMIZU, H., Proc. Eurodisplay 84, September 1984: A 210-288 Matrix LCD Controlled by Double Stage Diode Rings, p. 141 et seq., Paris; STROMER, M., Proc. Eurodisplay 84, September 1984: Design of Thin Film Transistors for Matrix Addressing of Television Liquid Crystal Displays, p. 145 et seq., Paris]. As the resistance decreases, the contrast of a matrix LCD display deteriorates, and the problem of “afterimage elimination” can arise. As the resistivity of the liquid crystal mixture generally decreases over the lifetime of a matrix LCD, owing to interaction with the interior surfaces of the display, a high (initial) resistance is very important to achieve acceptable service life. Particularly with low-voltage mixtures it has hitherto been impossible to achieve very high resistivities. Moreover, it is important for the resistivity to exhibit as low an increase as possible with increasing temperature and after thermal exposure and/or exposure to UV. A further particularly disadvantageous feature is the low-temperature properties of the prior art mixtures. It is desirable that no crystallization and/or smectic phases occur even at low temperatures and that viscosity temperature dependence be as small as possible.The prior art matrix LCDs therefore do not meet present-day requirements.

[0015] Therefore a great need is still present for matrix LCDs having very high resistivity and at the same time having a wide operating temperature range, short switching times even at low temperatures, and a low threshold voltage, which do not exhibit the drawbacks of the prior art or exhibit them only to a lesser extent.

[0016] For TN (Schadt-Helfrich) cells, media are desirable which permit the following advantages in these cells:

[0017] extended nematic phase domain (especially towards low temperatures)

[0018] switchability at extremely low temperatures (outdoor use, motor vehicles, avionics),

[0019] increased resistance to UV radiation (extended lifetime), and

[0020] low optical birefringence.

[0021] The media available from the prior art do not permit these advantages to be achieved while at the same time maintaining other parameters.

[0022] For supertwisted cells (STN), media are desirable which permit higher multiplexability and/or lower threshold voltages and/or wider nematic phase domains (especially at low temperatures). For this purpose, a further expansion of the available parameter space (clearing point, transition smectic-nematic or melting point, viscosity, dielectric parameters, elastic parameters) is urgently required.

[0023] It is an object of the invention to provide media especially for such matrix LCDs, TN or STN displays which do not exhibit the above-mentioned drawbacks or exhibit them only to a lesser extent, and preferably at the same time have very high resistivities and low threshold voltages. This object requires liquid-crystalline compounds having a high clearing point and low rotational viscosity.

[0024] We have found that this object can be achieved if the liquid-crystalline compounds according to the invention are employed.

[0025] The invention therefore relates to liquid-crystalline compounds of formula I,

[0026] wherein

[0027] R¹ is a straight-chain or branched alkyl radical having 1 to 15 C atoms which is unsubstituted, singly substituted by CN or CF₃, at least singly substituted by halogen, wherein optionally one or more CH₂ groups are substituted by —O—,—CO—,—S—, —CH═CH—, —C≡C—, —OC—O— or —O—CO— in such a way that O atoms are not directly linked together,

[0028] R² is CN, SF₅, H, F, Cl, NCS, SCN, or a straight-chain or branched alkyl radical having 1 to 15 C atoms which is unsubstituted, singly substituted by CN or CF₃, at least singly substituted by halogen, wherein optionally one or more CH₂ groups are substituted by —O—, —CO—, —S—, —CH═CH—, —C≡C—, —OC—O— or —O—CO— in such a way that O atoms are not directly linked together,

[0029] A¹, A², A³ and A⁴ are each, independently, a 1,4-cyclohexenylene radical in which one or two non-adjacent CH₂ groups are optionally replaced by —O— or—S—, a 1,4-phenylene radical in which one or two CH groups are optionally replaced by N, or a radical selected from piperidine-1,4-diyl, 1,4-bicyclo[2.2.2]octylene, naphthalene-2,6-diyl, decahyd ronaphthalene-2,6-diyl, and 1,2,3,4-tetrahydronaphthalene-2,6-diyl, wherein each is optionally singly substituted or polysubstituted by halogen,

[0030] Z¹ and Z² are each, independently, —CO—O—, —O—CO—, CF₂O—, —OCF₂—, —CH₂O—, —OCH₂—, —CH₂CH₂—, —(CH₂)₄—, —C₂F₄—, —CF₂CH₂—, —CH₂CF₂—, —CF═CF—, —CH═CH—, —C≡C— or a single bond,

[0031] a is 0, 1 or 2,

[0032] b is 0, 1 or 2, and

[0033] c is 0, 1 or 2,

[0034] wherein a+b+c≦2.

[0035] The invention further relates to the use of the compounds of formula I in liquid-crystalline media.

[0036] The compounds of formula I have a wide application range. Depending on the choice of substituents, these compounds can serve as base materials for liquid-crystalline media. Alternatively, compounds of the formula I can also be admixed to liquid-crystalline base materials from other classes of compounds, for example, in order to influence the dielectric and/or optical anisotropy of such a dielectric and/or to optimise its threshold voltage and/or its viscosity.

[0037] The compounds of formula I are colorless in their pure state and form liquid-crystalline mesophases in a temperature range favorable for electro-optical use. In particular, the compounds according to the invention are distinguished by their high clearing point and their low rotational viscosity values. They are stable chemically, thermally, and with respect to light.

[0038] The invention particularly relates to compounds of formula I, where R¹ is alkyl having from 1 to 10 C atoms, or an alkenyl radical having from 2 to 10 C atoms.

[0039] Preferred are compounds of formula I where c is 0. Z¹ and Z² are preferably a single bond, or alternatively —CF₂O—, —OCF₂—, —C₂F₄—, —CH₂O—, —OCH₂— or —COO—. Preferably a is 0.

[0040] If R¹ and/or R² is an alkyl radical and/or an alkoxy radical, this can be straight-chain or branched. Preferably it is straight-chain, has 2, 3, 4, 5, 6 or 7 C atoms, and therefore preferably is ethyl, propyl, butyl, pentyl, hexyl, heptyl, ethoxy, propoxy, butoxy, pentoxy, hexoxy, heptoxy, methyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, methoxy, octoxy, nonoxy, decoxy, undecoxy, dodecoxy, tridecoxy or tetradecoxy.

[0041] Oxaalkyl preferably is straight-chain 2-oxapropyl (=methoxymethyl), 2-(=ethoxymethyl) or 3-oxabutyl (=2-methoxyethyl), 2-, 3- or 4-oxapentyl, 2-, 3-, 4- or 5-oxahexyl, 2-, 3-, 4-, 5- or 6-oxaheptyl, 2-, 3-, 4-, 5-, 6-, or 7-oxaoctyl, 2-, 3-, 4-, 5-, 6-, 7- or 8-oxanonyl, or 2-, 3-, 4-, 5-, 6-, 7-, 8- or 9-oxadecyl.

[0042] If R¹ and/or R² is an alkenyl radical, it can be straight-chain or branched. Preferably it is straight-chain and has from 2 to 10 C atoms. It is therefore, in particular, vinyl, prop-1-, or prop-2-enyl, but-1-, 2- or but-3-enyl, pent-1-, 2-, 3- or pent-4-enyl, hex-1-, 2-, 3-, 4- or hex-5-enyl, hept-1-, 2-, 3-, 4-, 5- or hept-6-enyl, oct-1-, 2-, 3-, 4-, 5-, 6- or oct-7-enyl, non-1-, 2-, 3-, 6-, 7- or non-8-enyl, dec-1-, 2-, 3-, 4-, 5-, 6-, 7-, 8- or dec-9-enyl.

[0043] If R¹ and/or R² is an alkyl radical, in which one CH₂ group has been replaced by —O— and one by —CO—, these are preferably adjacent. These therefore comprise an acyloxy group —CO—O— or an oxycarbonyl group —CO—. Preferably, they are straight-chain and have from 2 to 6 C atoms.

[0044] In particular, they therefore are acetyloxy, propionyloxy, butyryloxy, pentanoyloxy, hexanoyloxy, acetyloxymethyl, propionyloxymethyl, butyryl-oxymethyl, pentanoyloxymethyl, 2-acetyloxyethyl, 2-propionyloxyethyl, 2-butyryloxyethyl, 3-acetyloxypropyl, 3-propionyloxypropyl, 4-acetyloxy-butyl, methoxycarbonyl, ethoxycarbonyl, propoxycarbonyl, butoxycarbonyl, pentoxycarbonyl, methoxycarbonylmethyl, ethoxycarbonylmethyl, propoxycarbonylmethyl, butoxycarbonylmethyl, 2-(methoxycarbonyl)ethyl, 2-(ethoxycarbonyl)ethyl, 2-(propoxycarbonyl)ethyl, 3-(methoxycarbonyl)-propyl, 3-(ethoxycarbonyl)propyl, or 4-(methoxycarbonyl)butyl.

[0045] If R¹ and/or R² is an alkyl or alkenyl radical singly substituted by CN or CF₃, said radical is preferably straight-chain. The substitution by CN or CF₃ can be in any position.

[0046] If R¹ and/or R2 is an alkyl or alkenyl radical at least singly substituted by halogen, said radical is preferably straight-chain and halogen is preferably F or Cl. In the case of polysubstitution, halogen is preferably F. The resulting radicals also include perfluorinated radicals. In the case of single substitution, the fluoro or chlorine substituent can be in any position, but preferably in the ω-position.

[0047] Compounds of formula I carrying branched pendant groups R¹ and/or R² are occasionally of interest because of their better solubility in the conventional liquid-crystalline base materials. In particular, however, they are of interest as chiral dopants if they are optically active. Smectic compounds of this type are suitable as components for ferroelectric materials.

[0048] Compounds of formula I having S_(A) phases are suitable, for example, for thermally addressed displays.

[0049] Branched groups of this type as a rule do not contain more than one chain branching. Preferred branched radicals R¹ and R² are isopropyl, 2-butyl (=1-methylpropyl), isobutyl (=2-methylpropyl), 2-methylbutyl, isopentyl (=3-methylbutyl), 2-methylpentyl, 3-methylpentyl, 2-ethylhexyl, 2-propylpentyl, isopropoxy, 2-methylpropoxy, 2-methylbutoxy, 3-methyl-butoxy, 2-methylpentoxy, 3-methylpentoxy, 2-ethylhexoxy, 1-methylhexoxy, 1-methylheptoxy.

[0050] R² is preferably H, F, Cl, CN, CF₃, SF₅, CF₂H, OCF₃, OCF₂H, OCFHCF₃, OCFHCFH₂, OCFHCF₂H, OCF₂CH₃, OCF₂CFH₂, OCF₂CF₂H, OCF₂CF₂CF₂H, OCF₂CF₂CFH₂, OCFHCF₂CF₃, OCFHCF₂CF₂H, OCFHCFHCF₃, OCH₂CF₂CF₃, OCF₂CF₂CF₃, OCF₂CFHCFH₂, OCF₂CH₂CF₂H, OCFHCF₂CFH₂, OCFHCFHCF₂H, OCFHCH₂CF₃, OCH₂CFHCF₃, OCH₂CF₂CF₂H, OCF₂CFHCH₃, OCF₂CH₂CFH₂, OCFHCF₂CH₃, OCFHCFHCFH₂, OCFHCH₂CF₃, OCH₂CF₂CFH₂, OCH₂CFHCF₂H, OCF₂CH₂CH₃, OCFHCFHCH₃, OCFHCH₂CFH₂, OCH₂CF₂CH₃, OCH₂CFHCFH₂, OCH₂CH₂CF₂H, OCHCH₂CH₃, OCH₂CFHCH₃, OCH₂CH₂CF₂H, OCClFCF₃, OCClFCClF₂, OCClFCFH₂, OCFHCCl₂F, OCClFCF₂H, OCClFCClF₂, OCF₂CClH₂, OCF₂CCl₂H, OCF₂CCl₂F, OCF₂CClFH, OCF₂CClF₂, OCF₂CF₂CClF₂, OCF₂CF₂CCl₂F, OCClFCF₂CF₃, OCClFCF₂CF₂H, OCClFCF₂CClF₂, OCClFCFHCF₃, OCClFCClFCF₃, OCCl₂CF₂CF₃, OCClHCF₂CF₃, OCClFCF₂CF₃, OCClFCClFCF₃, OCF₂CClFCFH₂, OCF₂CF₂CCl₂F, OCF₂CCl₂CF₂H, OCF₂CH₂CClF₂, OCClFCF₂CFH₂, OCFHCF₂CCl₂F, OCClFCFHCF₂H, OCClFCClFCF₂H, OCFHCFHCClF₂, OCClFCH₂CF₃, OCFHCCl₂CF₃, OCCl₂CFHCF₃, OCH₂CClFCF₃, OCCl₂CF₂CF₂H, OCH₂CF₂CClF₂, OCF₂CClFCH₃, OCF₂CFHCCl₂H, OCF₂CCl₂CFH₂, OCF₂CH₂CCl₂F, OCClFCF₂CH₃, OCFHCF₂CCl₂H, OCClFCClFCFH₂, OCFHCFHCCl₂F, OCClFCH₂CF₃, OCFHCCl₂CF₃, OCCl₂CF₂CFH₂, OCH₂CF₂CCl₂F, OCCl₂CFHCF₂H, OCClHCClFCF₂H, OCF₂CClHCClH₂, OCF₂CH₂CCl₂H, OCClFCFHCH₃, OCF₂CClFCCl₂H, OCClFCH₂CFH₂, OCFHCCl₂CFH₂, OCCl₂CF₂CH₃, OCH₂CF₂CClH₂, OCCl₂CFHCFH₂, OCH₂CClFCFCl₂, OCH₂CH₂CF₂H, OCClHCClHCF₂H, OCH₂CCl₂CF₂H, OCClFCH₂CH₃, OCFHCH₂CCl₂H, OCClHCFHCClH₂, OCH₂CFHCCl₂H, OCCl₂CH₂CF₂H, OCH₂CCl₂CF₂H, CH═CF₂, CF═CF₂, OCH═CF₂, OCF═CF₂, CH═CHF, OCH═CHF, CF═CHF, OCF=CHF, especially F, Cl, CN, CF₃, SF₅, CF₂H, OCF₃, OCF₂H, OCFHCF₃, OCFHCFH₂, OCFHCF₂H, OCF₂CH₃, OCF₂CFH₂, OCF₂CF₂H, OCF₂CF₂CF₂H, OCF₂CF₂CFH₂, OCFHCF₂C OCFHCF₂CF₂H, OCF₂CF₂CF₃, OCF₂CHFCF₃, OCClFCF₂CF₃.

[0051] For the sake of simplicity, hereinafter Cyc represents a 1,4-cyclohexylene radical, Che a 1,4-cyclohexenyl radical, Dio a 1,3-dioxane-2,5-diyl radical, Dit a 1,3-dithiane-2,5-diyl radical, Phe a 1,4-phenylene radical, Pyd a pyridine-2,5-diyl radical, Pyr a pyrimidine-2,5-diyl radical, Bi a bicyclo[2.2.2]octylene radical, PheF a 2- or 3-fluoro-1,4-phenylene radical, PheFF a 2,3-difluoro- or 2,6-difluoro-1,4-phenylene radical, Nap a substituted or unsubstituted naphthalene radical, Dec a decahydronaphthalene radical.

[0052] The compounds of the formula I accordingly comprise the preferred compounds having three rings of the subformulae Ia to If: R¹-Cyc-C₂F₄-Cyc-COO-Phe-R² la R¹-Cyc-C₂F₄-Cyc-COO-PheF-R² lb R¹-Cyc-C₂F₄-Cyc-COO-PheFF-R² lc R¹-Cyc-C₂F₄-Cyc-COO-Bi-R² ld R¹-Cyc-C₂F₄-Cyc-COO-Nap-R² le R¹-Cyc-C₂F₄-Cyc-COO-Dec-R² lf

[0053] Compounds having four rings of the subformulae Ik to Iw: R¹-Cyc-C₂F₄-Cyc-Cyc-COO-Phe-R² lk R¹-Cyc-C₂F₄-Cyc-Cyc-COO-PheF-R² ll R¹-Cyc-C₂F₄-Cyc-Cyc-COO-PheFF-R² lm R¹-Cyc-C₂F₄-Cyc-Cyc-COO-Nap-R² ln R¹-Cyc-C₂F₄-Cyc-Cyc-COO-Dec-R² lo R¹-Cyc-C₂F₄-Cyc-Cyc-COO-Bi-R² lp R¹-Cyc-C₂F₄-Cyc-Phe-COO-Phe-R² lq R¹-Cyc-C₂F₄-Cyc-Phe-COO-PheF-R² lr R¹-Cyc-C₂F₄-Cyc-Phe-COO-PheFF-R² ls R¹-Cyc-C₂F₄-Cyc-PheF-COO-Phe-R² lt R¹-Cyc-C₂F₄-Cyc-PheFF-COO-Phe-R² lu R¹-Cyc-C₂F₄-Cyc-PheFF-COO-PheFF-R² lv R¹-Cyc-C₂F₄-Cyc-COO-Phe-Cyc-R² lw

[0054] Particularly preferred among these are the compounds of the subformulae Ia, Ib and Ic.

[0055] In the compounds of the previous and following formulae, R² is preferably F, CN, OCF₃, OCHF₂, CF₃, OCHFCF₃, OC₂F₅ or OCF₂CHFCF₃, straight-chain alkyl or alkoxy.

[0056] R¹ is preferably straight-chain, unsubstituted alkyl, alkoxy, alkenyloxy or alkenyl having up to 10 C atoms.

[0057] A² is preferably Phe, PheF, PheFF, Cyc or Che, also Pyr or Dio, Dec or Nap. Preferably the compounds of formula I do not include more than one of the radicals Bi, Pyd, Pyr, Dio, Dit, Nap or Dec.

[0058] Preferred are compounds of formula I in which A¹ is a singly or doubly substituted 1,4-phenylene. In particular, these are 2-fluoro-1,4-phenylene, 3-fluoro-1,4-phenylene, 2,3-difluoro-1,4-phenylene and 2,6-difluoro-1,4-phenylene.

[0059] Preferred smaller groups of compounds of formula I are those of the subformulae 11 to 124:

[0060] where

[0061] R¹ has the meanings described previously and “alkyl” is a straight-chain or branched alkyl having 1-9 C atoms.

[0062] The compounds of the formula I are prepared in accordance with methods known per se, as described in the literature (e.g. in the standard textbooks such as Houben-Weyl, Methoden der Organischen Chemie, Georg-Thieme-Verlag, Stuttgart) specifically under reaction conditions known and suitable for these reactions. Variants known per se but not mentioned here in detail are also included.

[0063] The compounds according to the invention can, for example, be prepared as follows:

[0064] The invention also relates to electro-optical displays (in particular STN displays or matrix LCDs with two plane-parallel substrates which, together with a border, form a cell, which have integrated nonlinear elements for switching individual pixels on the substrates and, wherein a nematic liquid crystal mixture having positive dielectric anisotropy and high resistivity is present in the cell) which comprise media as described previously and to the use of these media for electro-optical purposes.

[0065] The liquid crystal mixture according to the invention permit considerable expansion of the available parameter space.

[0066] The media according to the invention achieve combinations of clearing point, optical anisotropy, viscosity at low temperature, thermal and UV stability and dielectric anisotropy far superior to current prior art materials.

[0067] So far it has not been possible to adequately meet the requirements of a high clearing point, a nematic phase at low temperature and a high Δε. While liquid-crystal mixtures such as e.g. MLC-6476 and MLC-6625 (Merck KGaA, Darmstadt, Germany) do exhibit comparable clearing points and low temperature stabilities, they have relatively high Δn values as well as higher threshold voltages of about ≧1.7 V.

[0068] Other mixture systems have comparable viscosities and values of Δε, but have clearing points around 60° C.

[0069] The liquid crystal mixtures according to the invention, while maintaining the nematic phase down to −20° C., preferably down to −30° C., and particularly preferably down to −40° C., make it possible to achieve clearing points above 80° C., preferably above 90° C., and particularly preferably above 100° C., with simultaneous dielectric anisotropy values of Δε≧4, and preferably ≧6 and a high specific resistivity, which makes possible excellent STN displays and matrix LCDs. The mixtures in particular are characterized by low operating voltages. The TN thresholds are below 1.5 V, preferably below 1.3 V.

[0070] It follows that with suitable choices for the components of the mixtures according to the invention one can achieve higher clearing points (e.g. above 110° C.) in conjunction with a higher threshold voltage, or lower clearing points in conjunction with lower threshold voltages while maintaining other advantageous properties. It is equally possible, in conjunction with a correspondingly small increase in viscosities, to obtain mixtures with a larger Δε and consequently lower thresholds. The matrix LCDs according to the invention preferably operate in the first transmission minimum according to Gooch and Tarry [C. H. Gooch and H. A. Tarry, Electron. Lett. 10, 2-4, 1974; C. H. Gooch and H. A. Tarry, Appl. Phys. Vol. 8, 1575-1584, 1975], resulting not only in particularly favorable electro-optical properties such as e.g. steep slope of the characteristic curve and low angular dependence of contrast (DE-C 3022818), but also a smaller dielectric anisotropy being sufficient in the second minimum in conjunction with a threshold voltage equal to that of an analogue display. Consequently it is possible, using the mixtures according to the invention, to achieve distinctly higher resistivities in the first minimum than with mixtures comprising cyano compounds. Those skilled in the art, using simple routine methods, are able, via a suitable choice of the individual components and their proportions by weight, to adjust the birefringence required for a predefined layer thickness of the matrix LCD.

[0071] The flow viscosity ν₂₀ at 20° C. is preferably <60 mm²·s⁻¹, particularly preferably <50 mm²·S⁻¹. The nematic phase domain is preferably at least 90°, in particular at least 100°. Preferably, this domain extends at least from −30° to +80°.

[0072] Measurements of the “capacity holding ratio” (HR) [S. Matsumoto et al., Liquid Crystals 5, 1320 (1989); K. Niwa et al., Proc. SID Conference, San Francisco, June 1984, p. 304 (1984); G. Weber et al., Liquid Crystals 5, 1381 (1989)] have shown that mixtures according to the invention comprising compounds of the formula I exhibit a distinctly smaller decrease in HR with increasing temperature than analogous mixtures comprising, instead of the compounds of the formula I, cyanophenylcyclohexanes of the formula

[0073] or esters of the formula

[0074] The UV stability of the mixtures according to the invention is likewise considerably better, i.e. they exhibit a distinctly smaller decrease in HR under exposure to UV.

[0075] Preferably, the media according to the invention are based on a plurality of (preferably two, three, four or more) compounds of formula I, i.e. the proportion of these compounds is 5-95%, preferably 10-60% and particularly preferably in the range of 15-40%.

[0076] Individual compounds of the formulae I to X (formulae II to X are described below) and their subformulae which can be used in the media according to the invention are either known or can be prepared in a manner similar to that of known compounds.

[0077] Preferred embodiments are specified below:

[0078] The medium preferably comprises 1, 2 or 3 homologous compounds of formula I, no more than 10% of each homologue being present in the mixture.

[0079] The medium comprises compounds of formula I where R¹ is preferably ethyl and/or propyl, alternatively butyl, pentyl, hexyl and heptyl. Compounds of formula I having short side chains R¹ have a positive effect on the elastic constants, especially K₁, and result in mixtures having particularly low threshold voltages.

[0080] The medium additionally comprises one or more compounds of formulae II to X:

[0081]  where the individual radicals have the following meanings:

[0082] R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 C atoms,

[0083] X⁰ is halogenated alkyl, halogenated alkenyl, halogenated alkenyloxy, halogenated alkoxy, each having up to 7 C atoms, F or Cl,

[0084] Z⁰ is —CH═CH—, —C₂H₄—, —C₂F₄—, —CF═CF—, —CF₂O—, —OCF₂— or —COO—,

[0085] Y¹, Y², Y³ and Y⁴ are, each independently, H or F, and

[0086] r is 0 or 1.

[0087] The compound of formula IV is preferably

[0088] The medium additionally comprises one or more compounds of the formulae

[0089] wherein R⁰ and Y² are as previously defined.

[0090] The medium preferably comprises one, two or three, alternatively four homologues of the compounds of H1 to H17 (n=1-7):

[0091] The medium additionally comprise one or more dioxanes of the formula DI and/or DII,

[0092] wherein R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 C atoms. Preferably R⁰ in the compounds of formula DI and/or DII is straight-chain alkyl or alkenyl having up to 7 C atoms.

[0093] The medium additionally comprises one or more compounds of formulae XI to XVI:

[0094] wherein R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 C atoms. X⁰ is F, Cl, halogenated alkyl, hologenated alkenyl, halogenated alkenyloxy or halogenated alkoxy having up to 7 C atoms. Y¹, Y², Y³ and Y⁴ are, each independently, H or F. X⁰ preferably is F, Cl, CF₃, OCF₃, OCHF₂. R⁰ preferably is alkyl, oxaalkyl, fluoroalkyl, alkenyl or alkenyloxy.

[0095] The proportion of compounds of formulae I to X together in the overall mixture is at least 50 wt %.

[0096] The proportion of compounds of formula I in the overall mixture is from 5 to 50 wt %.

[0097] The proportion of compounds of formulae II to X in the overall mixture is from 30 to 70 wt %.

[0098] The medium comprises compounds of formulae II , III, IV, V, VI, VII, VIII, IX and/or X.

[0099] R⁰ is straight-chain alkyl or alkenyl of 2 to 7 C atoms.

[0100] The medium essentially comprises compounds of the formulae II to XVI.

[0101] The medium comprises further compounds, preferably of formulae XVII to XX:

[0102] wherein R⁰ and X⁰ are as previously defined and the 1,4-phenylene rings can be CN—, chloro- or fluorosubstituted. Preferably, the 1,4-phenylene rings are singly substituted or polysubstituted by fluorine atoms.

[0103] The medium comprises further compounds, preferably of formulae RI to RX,

[0104] wherein

[0105] R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl each having up to 9 C atoms,

[0106] d is 0, 1 or 2,

[0107] Y¹ is H or F, Alkyl or

[0108] Alkyl* are, each independently, a straight-chain or branched alkyl radical having 1-9 C atoms, Alkenyl or

[0109] Alkenyl* are, each independently, a straight-chain or branched alkenyl radical having up to 9 C atoms.

[0110] The medium preferably comprises one or more compounds of the formulae

[0111] wherein n and m are each an integer of 1 to 9.

[0112] The proportion by weight of compounds of formula I: compounds of formulas (II+III+IV+V+VI+VII+VIII+IX+X) together is preferably from 1:10 to 10:1.

[0113] The medium essentially comprises compounds of formulae I to XVI.

[0114] It was found that even a relatively small proportion of the compounds of formula I mixed with conventional liquid crystal materials, but in particular with one or more compounds of formula II, III, IV, V, VI, VII, VIII, IX and/or X leads to a considerable decrease in the threshold voltage and to low values of the birefringence, wide-domain nematic phases with low smectic-nematic transition temperatures, thereby improving the storage stability. The compounds of the formulae I to X are colorless, stable and readily miscible with one another and with other liquid crystal materials.

[0115] The term “alkyl” or “alkyl*” encompasses straight-chain and branched alkyl groups having 1-9 carbon atoms, particularly the straight-chain groups methyl, ethyl, propyl, butyl, pentyl, hexyl and heptyl. Groups having 2-5 carbon atoms are preferred.

[0116] The term “alkenyl” or “alkenyl” encompasses straight-chain and branched alkenyl groups having up to 9 carbon atoms, preferably the straight-chain groups. Preferred alkenyl groups are C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl, C₅-C₇-4-alkenyl, C₆-C₇-5-alkenyl and C₇-6-alkenyl, especially preferred are C₂-C₇-1E-alkenyl, C₄-C₇-3E-alkenyl and C₅-C₇-4-alkenyl. Examples of preferred alkenyl groups are vinyl, 1E-propenyl, 1E-butenyl, 1E-pentenyl, 1E-hexenyl, 1E-heptenyl, 3-butenyl, 3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl, 4E-hexenyl, 4Z-heptenyl, 5-hexenyl, 6-heptenyl and the like. Groups having up to 5 carbon atoms are preferred.

[0117] The term “fluoroalkyl” preferably comprises straight-chain groups with terminal fluorine, i.e., fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl, 5-fluoropentyl, 6-fluorohexyl and 7-fluoroheptyl. Other positions of fluorine are not precluded, however.

[0118] The term “oxaalkyl” preferably comprises straight-chain radicals of the formula C_(n)H_(2n+1)—O—(CH₂)_(m), where n and m each, independently of one another, are 1 to 6. Preferably, n is 1 and m is 1 to 6.

[0119] By varying the choice for R⁰ and X⁰, one can modify the response times, the threshold voltage, the slope of the transmission characteristics etc. as desired. For example, 1E-alkenyl radicals, 3E-alkenyl radicals, 2E-alkenyloxy radicals and the like as a rule lead to shorter response times, improved nematic tendencies and a higher ratio of the elastic constants k₃₃ (bend) and k₁₁ (splay), compared with alkyl or alkoxy radicals. 4-Alkenyl radicals, 3-alkenyl radicals and the like generally result in lower threshold voltages and smaller values of k₃₃/k₁₁ than alkyl and alkoxy radicals.

[0120] A —CH₂CH₂— group in Z¹ generally leads to higher values of k₃₃/k₁₁, compared to a single covalent bond. Higher values of k₃₃/k₁₁ permit, for example, less steep transmission characteristics in TN cells with twists of 90° (to achieve grey hues) and steeper transmission characteristics in STN, SBE and OMI cells (higher multiplexability) and vice versa.

[0121] The optimal quantitative ratio of the compounds of the formula I to formulae II+III+IV+V+VI+VII+VII+IX+X largely depends on the desired characteristics, on the choice of components for the formulae I, II, III, IV, V, VI, VII, VIII, IX and/or X and on the choice of any further components. Suitable quantitative ratios within the above-specified range can readily be determined ad hoc.

[0122] The total quantity of compounds of the formulae I to XVI in the mixtures according to the invention is not critical. The mixtures can therefore comprise one or more further components, to optimize various properties. The observed effect on the response times and on the threshold voltage, however, is as a rule higher, the higher the overall concentration of compounds of the formulae I to XVI.

[0123] In a preferred embodiment, the media according to the invention comprise compounds of the formulae II to X (preferably II and/or III), where X⁰ is OCF₃, OCHF₂, F, OCH═CF₂, OCF═CF₂, OCF₂CHFCF₃ or OCF₂—CF₂H. A beneficial synergistic effect with the compounds of formula I results in particularly advantageous properties.

[0124] The mixtures according to the invention having low optical anisotropy (Δn<0.07) are particularly suitable for reflective displays. Low V_(th) mixtures are especially suitable for 3.3 V drivers and also for 4V or 5V drivers. Mixtures free from esters are preferred for the latter applications.

[0125] In the present application and in the following examples, the construction of the matrix LCD according to the invention comprising polarizers, electrode baseplates and electrodes with a surface treatment corresponds to the standard design of such displays. Within the present context, the term “standard design” is comprehensive and additionally covers any variations and modifications of the matrix LCD, including in particular matrix display elements on the basis of poly-Si TFT or MIM.

[0126] An essential difference between the displays according to the invention and the current customary displays based on the twisted nematic cell is the choice of liquid crystal parameters of the liquid crystal layer.

[0127] The preparation of the liquid crystal mixtures which can be used according to the invention is carried out by methods which are customary per se. As a rule, the desired quantity of the components used in smaller amounts is dissolved in the component which constitutes the main ingredient, preferably at an elevated temperature. An alternative procedure is to mix solutions of the components in an organic solvent, e.g. in acetone, chloroform or methanol, and then, after thorough mixing, to remove the solvent again, for example by distillation.

[0128] The dielectrics can also comprise further additives known to those skilled in the art and described in the literature. For example, 0-15% of pleochroic dyes or chiral dopants can be added.

[0129] C refers to a crystalline phase, S to a smectic phase, S_(c) to a smectic phase, N to a nematic phase and I to the isotropic phase.

[0130] V₁₀ denotes the voltage for 10% transmission (viewing direction perpendicular to the substrate surface). t_(on) denotes the on and t_(off) the off time at an operating voltage corresponding to 2.0 times the value of V₁₀. Δn denotes the optical anisotropy and n₀ the refractive index. Δε denotes the dielectric anisotropy (Δε=ε_(II)−ε_(⊥), where ε_(II) refers to the dielectric constant parallel to the longitudinal axes of the molecule and ε_(⊥)is the dielectric constant perpendicular thereto). The electro-optical data were ID measured in a TN cell in the 1st minimum (i.e. at a d·Δn value of 0.5) at 20° C., unless explicitly stated otherwise. The optical data were measured at 20° C., unless explicitly stated otherwise.

[0131] In the present application and in the following examples the structures of the liquid crystal compounds are specified by acronyms, which can be transformed into chemical formulae according to the following Tables A and B. All the radicals C_(n)H_(2n+1) and C_(m)H_(2m+1) are straight-chain alkyl radicals having n or m C atoms. n and m, independently of one another, denote 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14 or 15. The coding according to Table B is self-evident. Table A specifies the acronym for the parent body Only. In individual cases, the acronym for the parent body is followed, separated therefrom by a hyphen, by a code for the substituents R¹, R², L¹ and L²: Code for R¹, R², L¹, L² R¹ R² L¹ L² Nm C_(n)H_(2n+1) C_(m)H_(2m+1) H H NOm C_(n)H_(2n+1) OC_(m)H_(2m+1) H H NO.m OC_(n)H_(2n+1) C_(m)H_(2m+1) H H N C_(n)H_(2n+1) CN H H

[0132] Code for R¹, R², L¹, L² R¹ R² L¹ L² nN.F C_(n)H_(2n+1) CN H F NF C_(n)H_(2n+1) F H H NOF OC_(n)H_(2n+1) F H H NCl C_(n)H_(2n+1) Cl H H nF.F C_(n)H_(2n+1) F H F nF.F.F C_(n)H_(2n+1) F F F NCF₃ C_(n)H_(2n+1) CF₃ H H nOCF₃ C_(n)H_(2n+1) OCF₃ H H nOCF₂ C_(n)H_(2n+1) OCHF₂ H H NS C_(n)H_(2n+1) NCS H H rVsN C_(r)H_(2r+1)—CH═CH—C_(s)H_(2s−) CN H H rEsN C_(r)H_(2r+1)—O—C₂H_(2s−) CN H H NAm C_(n)H_(2n+1) COOC_(m)H_(2m+1) H H nOCCF₂.F.F C_(n)H_(2n+1) OCH₂CF₂H F F

[0133] Preferred mixture components are listed in Tables A and B. TABLE A

PYP

PYRP

BCH

CBC

CCH

CCP

CPTP

CEPTP

ECCP

CECP

EPCH

PCH

PTP

BECH

EBCH

CPC

B

FET-nF

CGG

CGU

CUP

[0134] TABLE B

CBC-nmF

PCH-nOm

FET-nCl

CP-nOCF₃

CCH-nOm

BCH-n.Fm

Inm

CBC-nmF

ECCP-nm

CCH-n1EM

T-nFm

CGU-n-F

CCP-nOCF₃.F

CGG-n-F

CCP-nOCF₂.F(.F)

CCP-nF.F.F

CGU-n-OXF

CUZU-n-F

CGU-n-O1DT

CCZU-n-F

CC-n-V1

CC-n-V

CCP-nOCF₃

BCH-nF.F.F

CWCZU-n-F

CWCZG-n-F

CCOC-n-m

CGZU-n-F

CUZP-n-F

CGU-1V-F

CCG-V-F

CGZP-n-F

UZP-n-N

CGZP-n-OT

CUZP-n-OT

CCQU-n-F

Dec-U-n-F

Nap-U-n-F

CWGZG-n-F

CWCZG-n-OT

CWCZP-n-OT

[0135] Table C lists possible dopants which can be added to the mixtures according to the invention. TABLE C

C 15

CB 15

CM 21

R/S 811

CM 44

CM 45

CM 47

CN

R/S-1011

R/S-2011

R/S-3011

R/S-4011

[0136] Table D lists exemplary stabilizers which can be added to the mixtures according to the invention. TABLE D

[0137] The following examples are intended to illustrate the invention without limiting it. Hereinbefore and hereinafter, percentages are given in percent by weight. All temperatures are specified in degrees centigrade. M.p. means melting point, c.p. means clearing point, C means crystalline state, N means nematic phase, S means smectic phase, and I means isotropic phase. Data appearing between these symbols represent the transition temperatures. Δn means optical anisotropy (589 nm, 20° C.). The flow viscosity ν₂₀ (mm²/sec) and the rotational viscosity γ₁ [mPa.s] were each determined at 20° C.

[0138] “Standard work-up” means: water is added if required, the mixture is extracted with dichloromethane, diethyl ether, methyl tert-butyl ether or toluene, followed by phase separation, then drying of the organic phase, evaporation of the solvent and purification of the product by distillation under reduced pressure or crystallization and/or chromatography. The following abbreviations are used: n-BuLi 1.6 molar solution of n-butyllithium in n-hexane DMAP 4-(dimethylamino)pyridine THF tetrahydrofuran DCC N,N′-dicyclohexylcarbodiimide

[0139] Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize the present invention to its fullest extent. The following preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever.

[0140] The entire disclosureof all applications, patents and publications, cited above or below, and of corresponding German application No. 10064996.3, filed Dec. 23, 2001 is hereby incorporated by reference.

EXAMPLE 1

[0141] Step 1.1

[0142] 3.494 mol of 1,2-bis(4-hydroxyphenyl)tetrafluoroethane is dissolved in 15 l of isopropanol and hydrogenated with 400 g of 5% rhodium activated carbon at 60° C. and 5 bar. After the hydrogenation is complete, the catalyst is filtered off, the filtrate is concentrated and the residue is recrystallized from ethyl acetate.

[0143] Step 1.2

[0144] 1.5 mol of pyridinium chlorochromate, 300 g of Celite® 545, (Celite® 545 is an additive used to prevent clogging during filtration, it comprises kieselguhr, i.e., diatomaceous earth), in 4 l of dichloromethane and 0.97 mol of A are stirred overnight at room temperature. The suspension is then filtered off with suction, washed with dichloromethane and is concentrated. The residue is stirred with 50 ml of petroleum ether/ethyl acetate (1:1), 1 g of activated carbon and 5 g of silica gel and is then filtered off with suction over silica gel. The filtrate is dissolved in dichloromethane and is stirred overnight with 25 g of pyridine: sulfur trioxide complex. Finally, the mixture is extracted with water and filtered off with suction over silica gel. M.p. is 125-126° C. (methylcyclohexane, i.e., product was recrystallized from methylcyclohexane before determination of the metling point).

[0145] Step 1.3

[0146] 0.075 mol of B, and 0.230 mol of 2,2-dimethyl-1,3-propane in 250 ml of cyclohexane are stirred at 60° C. for 24 h with 0.05 g of sulfuric acid and 250 ml of water. The mixture is allowed to cool to room temperature and the sediment is separated from the liquid phase by means of a sintered disc and is dried. The melting range is 146-158° C. (methylcyclohexane)

[0147] Step 1.4

[0148] 0.121 mol of C and 0.145 mol of pentyltriphenylphosphonium bromide in 400 ml of anhydrous THF are cooled to −10° C. and admixed, with stirring, with 0.160 mol of potassium t-butylate in 100 ml of anhydrous THF. The reaction solution is stirred overnight at room temperature. This is followed by standard work-up. The crude product together with n-hexane is filtered off with suction over silica gel. The filtrate is concentrated and the residue is dissolved in 600 ml of THF. 8 g of Pd—C (5%) are added, followed by hydrogenation at 1 bar at room temperature.

[0149] Step 1.5

[0150] 0.041 mol of D, 300 ml of toluene and 100 ml of formic acid are stirred for 2 days at room temperature. The formic acid phase is diluted with water, extracted with toluene, and the combined toluene phases are finally subjected fo standard work-up. The melting range is 64-86.1° C. (methylcyclohexane)

[0151] Step 1.6

[0152] 0.105 mol of E, and 0.119 mol of methoxymethyltriphenylphosphonium chloride are produced as an initial charge in 450 ml of THF, and a solution of 0.134 mol of potassium t-butylate in 150 ml of THF is added dropwise with ice cooling. The reaction mixture is stirred overnight at room temperature, and the mixture is finally subjected to standard work-up.

[0153] Step 1.7

[0154] 0.061 mol of F, and 2.915 mol of formic acid in 200 ml of toluene are stirred overnight at room temperature. The mixture is then subjected to standard work-up.

[0155] To carry out the isomerization, 0.083 mol of the product, 600 ml of methanol and 0.135 mol of sodium hydroxide solution are stirred for 2 h at room temperature, followed by stirring for a further 2 h at −20° C. The precipitated product is filtered off with suction and washed with methanol.

[0156] Step 1.8

[0157] 0.042 mol of G in 300 ml of acetone are admixed at room temperature with 0.107 mol of chromic acid. The mixture is stirred at room temperature for 24 h. The excess of CrO₃ is removed with isopropanol. The reaction mixture is subjected to standard work-up. The crude product is recrystallized from acetone at 0° C. C ? S_(X) 253 N 258 I.

[0158] Step 1.9

[0159] 0.009 mol of H, 0.009 mol of 3,4,5-trifluorophenol and 0.010 mol of 4-(dimethylamino)pyridine are introduced as an initial charge in 30 ml of toluene. Added dropwise to this mixture at 10° C. is 0.010 mol of N,N-dicyclohexylcarbodiimide in 10 ml of toluene. The reaction mixture is stirred at room temperature for 48 h and is then admixed with 1.586 mmol of oxalic acid dihydrate and stirred for a further hour.

[0160] The product is filtered off with suction over silica gel and the filtrate is concentrated. The crude product is purified via a silica gel column (petroleum ether/MTB ether 9:1). The product is recrystallized from n-heptane.

[0161] C 47 S_(B) 109 N 173.2 I; Δε=8.8; Δn=0.724, γ₁=342

[0162] The following compounds of the formula

[0163] are prepared in a similar manner: R¹ R² L¹ L² CH₃ F H H CH₃ F F H CH₃ F F F C₂H₅ F H H C₂H₅ F F H C₂H₅ F F F n-C₃H₇ F H H n-C₃H₇ F F H n-C₃H₇ F F F n-C₄H₉ F H H n-C₄H₉ F F H n-C₄H₉ F F F n-C₅H₁₁ F H H n-C₅H₁₁ F F H n-C₆H₁₃ F H H n-C₆H₁₃ F F H n-C₆H₁₃ F F F n-C₇H₁₃ F H H n-C₇H₁₃ F F H n-C₇H₁₃ F F F CH₂═CH F H H CH₂═CH F F H CH₂═CH F F F CH₃CH═CH F H H CH₃CH═CH F F H CH₃CH═CH F F F CH₂═CHC₂H₄ F H H CH₂═CHC₂H₄ F F H CH₂═CHC₂H₄ F F F CH₃CH═CHC₂H₄ F H H CH₃CH═CHC₂H₄ F F H CH₃CH═CHC₂H₄ F F F (CH₃)₂CH F H H (CH₃)₂CH F F H (CH₃)₂CH F F F (CH₃)₂CHCH₂ F H H (CH₃)₂CHCH₂ F F H (CH₃)₂CHCH₂ F F F CH₃ OCF₃ H H CH₃ OCF₃ F H CH₃ OCF₃ F F C₂H₅ OCF₃ H H C₂H₅ OCF₃ F H C₂H₅ OCF₃ F F n-C₃H₇ OCF₃ H H n-C₃H₇ OCF₃ F H n-C₃H₇ OCF₃ F F n-C₄H₉ OCF₃ H H n-C₄H₉ OCF₃ F H n-C₄H₉ OCF₃ F F n-C₅H₁₁ OCF₃ H H n-C₅H₁₁ OCF₃ F H n-C₅H₁₁ OCF₃ F F n-C₆H₁₃ OCF₃ H H n-C₆H₁₃ OCF₃ F H n-C₆H₁₃ OCF₃ F F n-C₇H₁₅ OCF₃ H H n-C₇H₁₅ OCF₃ F H n-C₇H₁₅ OCF₃ F F CH₂═CH OCF₃ H H CH₂═CH OCF₃ F H CH₂═CH OCF₃ F F CH₃CH═CH OCF₃ H H CH₃CH═CH OCF₃ F H CH₃CH═CH OCF₃ F F CH₂═CHC₂H₄ OCF₃ H H CH₂═CHC₂H₄ OCF₃ F H CH₂═CHC₂H₄ OCF₃ F F CH₃CH═CHC₂H₄ OCF₃ H H CH₃CH═CHC₂H₄ OCF₃ F H CH₃CH═CHC₂H₄ OCF₃ F F (CH₃)₂CH OCF₃ H H (CH₃)₂CH OCF₃ F H (CH₃)₂CH OCF₃ F F (CH₃)₂CHCH₂ OCF₃ H H (CH₃)₂CHCH₂ OCF₃ F H (CH₃)₂CHCH₂ OCF₃ F F CH₃ OCHFCF₃ H H CH₃ OCHFCF₃ F H CH₃ OCHFCF₃ F F C₂H₅ OCHFCF₃ H H C₂H₅ OCHFCF₃ F H C₂H₅ OCHFCF₃ F F n-C₃H₇ OCHFCF₃ H H n-C₃H₇ OCHFCF₃ F H n-C₃H₇ OCHFCF₃ F F n-C₄H₉ OCHFCF₃ H H n-C₄H₉ OCHFCF₃ F H n-C₄H₉ OCHFCF₃ F F n-C₅H₁₁ OCHFCF₃ H H n-C₅H₁₁ OCHFCF₃ F H n-C₅H₁₁ OCHFCF₃ F F n-C₆H₁₃ OCHFCF₃ H H n-C₆H₁₃ OCHFCF₃ F H n-C₆H₁₃ OCHFCF₃ F F CH₂═CH OCHFCF₃ H H CH₂═CH OCHFCF₃ F H CH₂═CH OCHFCF₃ F F CH₃CH═CH OCHFCF₃ H H CH₃CH═CH OCHFCF₃ F H CH₃CH═CH OCHFCF₃ F F CH₂═CHC₂H₄ OCHFCF₃ H H CH₂═CHC₂H₄ OCHFCF₃ F H CH₂═CHC₂H₄ OCHFCF₃ F F CH₃CH═CHC₂H₄ OCHFCF₃ H H CH₃CH═CHC₂H₄ OCHFCF₃ F H CH₃CH═CHC₂H₄ OCHFCF₃ F F (CH₃)₂CH OCHFCF₃ H H (CH₃)₂CH OCHFCF₃ F H (CH₃)₂CH OCHFCF₃ F F (CH₃)₂CHCH₂ OCHFCF₃ H H (CH₃)₂CHCH₂ OCHFCF₃ F H (CH₃)₂CHCH₂ OCHFCF₃ F F CH₃ OCF₂CHFCF₃ H H CH₃ OCF₂CHFCF₃ F H CH₃ OCF₂CHFCF₃ F F C₂H₅ OCF₂CHFCF₃ H H C₂H₅ OCF₂CHFCF₃ F H C₂H₅ OCF₂CHFCF₃ F F n-C₃H₇ OCF₂CHFCF₃ H H n-C₃H₇ OCF₂CHFCF₃ F H n-C₃H₇ OCF₂CHFCF₃ F F n-C₄H₉ OCF₂CHFCF₃ H H n-C₄H₉ OCF₂CHFCF₃ F H n-C₄H₉ OCF₂CHFCF₃ F F n-C₅H₁₁ OCF₂CHFCF₃ H H n-C₅H₁₁ OCF₂CHFCF₃ F H n-C₅H₁₁ OCF₂CHFCF₃ F F n-C₆H₁₃ OCF₂CHFCF₃ H H n-C₆H₁₃ OCF₂CHFCF₃ F H n-C₆H₁₃ OCF₂CHFCF₃ F F CH₂═CH OCF₂CHFCF₃ H H CH₂═CH OCF₂CHFCF₃ F H CH₂═CH OCF₂CHFCF₃ F F CH₃CH═CH OCF₂CHFCF₃ H H CH₃CH═CH OCF₂CHFCF₃ F H CH₃CH═CH OCF₂CHFCF₃ F F CH₂═CHC₂H₄ OCF₂CHFCF₃ H H CH₂═CHC₂H₄ OCF₂CHFCF₃ F H CH₂═CHC₂H₄ OCF₂CHFCF₃ F F CH₃CH═CHC₂H₄ OCF₂CHFCF₃ H H CH₃CH═CHC₂H₄ OCF₂CHFCF₃ F H CH₃CH═CHC₂H₄ OCF₂CHFCF₃ F F (CH₃)₂CH OCF₂CHFCF₃ H H (CH₃)₂CH OCF₂CHFCF₃ F H (CH₃)₂CH OCF₂CHFCF₃ F F (CH₃)₂CHCH₂ OCF₂CHFCF₃ H H (CH₃)₂CHCH₂ OCF₂CHFCF₃ F H (CH₃)₂CHCH₂ OCF₂CHFCF₃ F F CH₃ OCHF₂ H H CH₃ OCHF₂ F H CH₃ OCHF₂ F F C₂H₅ OCHF₂ H H C₂H₅ OCHF₂ F H C₂H₅ OCHF₂ F F n-C₃H₇ OCHF₂ H H n-C₃H₇ OCHF₂ F H n-C₃H₇ OCHF₂ F F n-C₄H₉ OCHF₂ H H n-C₄H₉ OCHF₂ F H n-C₄H₉ OCHF₂ F F n-C₅H₁₁ OCHF₂ H H n-C₅H₁₁ OCHF₂ F H n-C₅H₁₁ OCHF₂ F F n-C₆H₁₃ OCHF₂ H H n-C₆H₁₃ OCHF₂ F H n-C₆H₁₃ OCHF₂ F F CH₂═CH OCHF₂ H H CH₂═CH OCHF₂ F H CH₂═CH OCHF₂ F F CH₃CH═CH OCHF₂ H H CH₃CH═CH OCHF₂ F H CH₃CH═CH OCHF₂ F F CH₂═CHC₂H₄ OCHF₂ H H CH₂═CHC₂H₄ OCHF₂ F H CH₂═CHC₂H₄ OCHF₂ F F CH₃CH═CHC₂H₄ OCHF₂ H H CH₃CH═CHC₂H₄ OCHF₂ F H CH₃CH═CHC₂H₄ OCHF₂ F F (CH₃)₂CH OCHF₂ H H (CH₃)₂CH OCHF₂ F H (CH₃)₂CH OCHF₂ F F (CH₃)₂CHCH₂ OCHF₂ H H (CH₃)₂CHCH₂ OCHF₂ F H (CH₃)₂CHCH₂ OCHF₂ F F CH₃ CF₃ H H CH₃ CF₃ F H CH₃ CF₃ F F C₂H₅ CF₃ H H C₂H₅ CF₃ F H C₂H₅ CF₃ F F n-C₃H₇ CF₃ H H n-C₃H₇ CF₃ F H n-C₃H₇ CF₃ F F n-C₄H₉ CF₃ H H n-C₄H₉ CF₃ F H n-C₄H₉ CF₃ F F n-C₅H₁₁ CF₃ H H n-C₅H₁₁ CF₃ F H n-C₅H₁₁ CF₃ F F n-C₆H₁₃ CF₃ H H n-C₆H₁₃ CF₃ F H n-C₆H₁₃ CF₃ F F CH₂═CH CF₃ H H CH₂═CH CF₃ F H CH₂═CH CF₃ F F CH₃CH═CH CF₃ H H CH₃CH═CH CF₃ F H CH₃CH═CH CF₃ F F CH₂═CHC₂H₄ CF₃ H H CH₂═CHC₂H₄ CF₃ F H CH₂═CHC₂H₄ CF₃ F F CH₃CH═CHC₂H₄ CF₃ H H CH₃CH═CHC₂H₄ CF₃ F H CH₃CH═CHC₂H₄ CF₃ F F (CH₃)₂CH CF₃ H H (CH₃)₂CH CF₃ F H (CH₃)₂CH CF₃ F F (CH₃)₂CHCH₂ CF₃ H H (CH₃)₂CHCH₂ CF₃ F H (CH₃)₂CHCH₂ CF₃ F F CH₃ CN H H CH₃ CN F H CH₃ CN F F C₂H₅ CN H H C₂H₅ CN F H C₂H₅ CN F F n-C₃H₇ CN H H n-C₃H₇ CN F H n-C₃H₇ CN F F n-C₄H₉ CN H H n-C₄H₉ CN F H n-C₄H₉ CN F F n-C₅H₁₁ CN H H n-C₅H₁₁ CN F H n-C₅H₁₁ CN F H n-C₆H₁₃ CN H H n-C₆H₁₃ CN F H nC₆H₁₃ CN F F CH₂═CH CN H H CH₂═CH CN F H CH₂═CH CN F F CH₃CH═CH CN H H CH₃CH═CH CN F H CH₃CH═CH CN F F CH₂═CHC₂H₄ CN H H CH₂═CHC₂H₄ CN F H CH₂═CHC₂H₄ CN F F CH₃CH═CHC₂H₄ CN H H CH₃CH═CHC₂H₄ CN F H CH₃CH═CHC₂H₄ CN F F (CH₃)₂CH CN H H (CH₃)₂CH CN F H (CH₃)₂CH CN F F (CH₃)₂CHCH₂ CN H H (CH₃)₂CHCH₂ CN F H (CH₃)₂CHCH₂ CN F F CH₃ SF₅ H H CH₃ SF₅ F H CH₃ SF₅ F F C₂H₅ SF₅ H H C₂H₅ SF₅ F H C₂H₅ SF₅ F F n-C₃H₇ SF₅ H H n-C₃H₇ SF₅ F H n-C₃H₇ SF₅ F F n-C₄H₉ SF₅ H H n-C₄H₉ SF₅ F H n-C₄H₉ SF₅ F F n-C₅H₁₁ SF₅ H H n-C₅H₁₁ SF₅ F H n-C₅H₁₁ SF₅ F F n-C₆H₁₃ SF₅ H H n-C₆H₁₃ SF₅ F H n-C₆H₁₃ SF₅ F F CH₂═CH SF₅ H H CH₂═CH SF₅ F H CH₂═CH SF₅ F F CH₃CH═CH SF₅ H H CH₃CH═CH SF₅ F H CH₃CH═CH SF₅ F F CH₂═CHC₂H₄ SF₅ H H CH₂═CHC₂H₄ SF₅ F H CH₂═CHC₂H₄ SF₅ F F CH₃CH═CHC₂H₄ SF₅ H H CH₃CH═CHC₂H₄ SF₅ F H CH₃CH═CHC₂H₄ SF₅ F F (CH₃)₂CH SF₅ H H (CH₃)₂CH SF₅ F H (CH₃)₂CH SF₅ F F (CH₃)₂CHCH₂ SF₅ H H (CH₃)₂CHCH₂ SF₅ F H (CH₃)₂CHCH₂ SF₅ F F CH₃ OCH═CF₂ H H CH₃ OCH═CF₂ F H CH₃ OCH═CF₂ F F C₂H₅ OCH═CF₂ H H C₂H₅ OCH═CF₂ F H C₂H₅ OCH═CF₂ F F n-C₃H₇ OCH═CF₂ H H n-C₃H₇ OCH═CF₂ F H n-C₃H₇ OCH═CF₂ F F n-C₄H₉ OCH═CF₂ H H n-C₄H₉ OCH═CF₂ F H n-C₄H₉ OCH═CF₂ F F n-C₅H₁₁ OCH═CF₂ H H n-C₅H₁₁ OCH═CF₂ F H n-C₅H₁₁ OCH═CF₂ F F n-C₆H₁₃ OCH═CF₂ H H n-C₆H₁₃ OCH═CF₂ F H n-C₆H₁₃ OCH═CF₂ F F CH₂═CH OCH═CF₂ H H CH₂═CH OCH═CF₂ F H CH₂═CH OCH═CF₂ F F CH₃CH═CH OCH═CF₂ H H CH₃CH═CH OCH═CF₂ F H CH₃CH═CH OCH═CF₂ F F CH₂═CHC₂H₄ OCH═CF₂ H H CH₂═CHC₂H₄ OCH═CF₂ F H CH₂═CHC₂H₄ OCH═CF₂ F F CH₃CH═CHC₂H₄ OCH═CF₂ H H CH₃CH═CHC₂H₄ OCH═CF₂ F H CH₃CH═CHC₂H₄ OCH═CF₂ F F (CH₃)₂CH OCH═CF₂ H H (CH₃)₂CH OCH═CF₂ F H (CH₃)₂CH OCH═CF₂ F F (CH₃)₂CHCH₂ OCH═CF₂ H H (CH₃)₂CHCH₂ OCH═CF₂ F H (CH₃)₂CHCH₂ OCH═CF₂ F F CH₃ CH═CF₂ H H CH₃ CH═CF₂ F H CH₃ CH═CF₂ F F C₂H₅ CH═CF₂ H H C₂H₅ CH═CF₂ F H C₂H₅ CH═CF₂ F F n-C₃H₇ CH═CF₂ H H n-C₃H₇ CH═CF₂ F H n-C₃H₇ CH═CF₂ F F n-C₄H₉ CH═CF₂ H H n-C₄H₉ CH═CF₂ F H n-C₄H₉ CH═CF₂ F F n-C₅H₁₁ CH═CF₂ H H n-C₅H₁₁ CH═CF₂ F H n-C₅H₁₁ CH═CF₂ F F n-C₆H₁₃ CH═CF₂ H H n-C₆H₁₃ CH═CF₂ F H n-C₆H₁₃ CH═CF₂ F F CH₂═CH CH═CF₂ H H CH₂═CH CH═CF₂ F H CH₂═CH CH═CF₂ F F CH₃CH═CH CH═CF₂ H H CH₃CH═CH CH═CF₂ F H CH₃CH═CH CH═CF₂ F F CH₂═CHC₂H₄ CH═CF₂ H H CH₂═CHC₂H₄ CH═CF₂ F H CH₂═CHC₂H₄ CH═CF₂ F F CH₃CH═CHC₂H₄ CH═CF₂ H H CH₃CH═CHC₂H₄ CH═CF₂ F H CH₃CH═CHC₂H₄ CH═CF₂ F F (CH₃)₂CH CH═CF₂ H H (CH₃)₂CH CH═CF₂ F H (CH₃)₂CH CH═CF₂ F F (CH₃)₂CHCH₂ CH═CF₂ H H (CH₃)₂CHCH₂ CH═CF₂ F H (CH₃)₂CHCH₂ CH═CF₂ F F CH₃ CF═CF₂ H H CH₃ CF═CF₂ F H CH₃ CF═CF₂ F F C₂H₅ CF═CF₂ H H C₂H₅ CF═CF₂ F H C₂H₅ CF═CF₂ F F n-C₃H₇ CF═CF₂ H H n-C₃H₇ CF═CF₂ F H n-C₃H₇ CF═CF₂ F F n-C₄H₉ CF═CF₂ H H n-C₄H₉ CF═CF₂ F H n-C₄H₉ CF═CF₂ F F n-C₅H₁₁ CF═CF₂ H H n-C₅H₁₁ CF═CF₂ F H n-C₅H₁₁ CF═CF₂ F F n-C₆H₁₃ CF═CF₂ H H n-C₆H₁₃ CF═CF₂ F H n-C₆H₁₃ CF═CF₂ F F CH₂═CH CF═CF₂ H H CH₂═CH CF═CF₂ F H CH₂═CH CF═CF₂ F F CH₃CH═CH CF═CF₂ H H CH₃CH═CH CF═CF₂ F H CH₃CH═CH CF═CF₂ F F CH₂═CHC₂H₄ CF═CF₂ H H CH₂═CHC₂H₄ CF═CF₂ F H CH₂═CHC₂H₄ CF═CF₂ F F CH₃CH═CHC₂H₄ CF═CF₂ H H CH₃CH═CHC₂H₄ CF═CF₂ F H CH₃CH═CHC₂H₄ CF═CF₂ F F (CH₃)₂CH CF═CF₂ H H (CH₃)₂CH CF═CF₂ F H (CH₃)₂CH CF═CF₂ F F (CH₃)₂CHCH₂ CF═CF₂ H H (CH₃)₂CHCH₂ CF═CF₂ F H (CH₃)₂CHCH₂ CF═CF₂ F F CH₃ OCF═CF₂ H H CH₃ OCF═CF₂ F H CH₃ OCF═CF₂ F F C₂H₅ OCF═CF₂ H H C₂H₅ OCF═CF₂ F H C₂H₅ OCF═CF₂ F F n-C₃H₇ OCF═CF₂ H H n-C₃H₇ OCF═CF₂ F H n-C₃H₇ OCF═CF₂ F F n-C₄H₉ OCF═CF₂ H H n-C₄H₉ OCF═CF₂ F H n-C₄H₉ OCF═CF₂ F F n-C₅H₁₁ OCF═CF₂ H H n-C₅H₁₁ OCF═CF₂ F H n-C₅H₁₁ OCF═CF₂ F F n-C₆H₁₃ OCF═CF₂ H H n-C₆H₁₃ OCF═CF₂ F H n-C₆H₁₃ OCF═CF₂ F F CH₂═CH OCF═CF₂ H H CH₂═CH OCF═CF₂ F H CH₂═CH OCF═CF₂ F F CH₃CH═CH OCF═CF₂ H H CH₃CH═CH OCF═CF₂ F H CH₃CH═CH OCF═CF₂ F F CH₂═CHC₂H₄ OCF═CF₂ H H CH₂═CHC₂H₄ OCF═CF₂ F H CH₂═CHC₂H₄ OCF═CF₂ F F CH₃CH═CHC₂H₄ OCF═CF₂ H H CH₃CH═CHC₂H₄ OCF═CF₂ F H CH₃CH═CHC₂H₄ OCF═CF₂ F F (CH₃)₂CH OCF═CF₂ H H (CH₃)₂CH OCF═CF₂ F H (CH₃)₂CH OCF═CF₂ F F (CH₃)₂CHCH₂ OCF═CF₂ H H (CH₃)₂CHCH₂ OCF═CF₂ F H (CH₃)₂CHCH₂ OCF═CF₂ F F

[0164] Examples of Mixtures Example M1 BCH-3F.F 10.80% Clearing point [° C.]: 98.2 BCH-5F.F 9.00% d · Δn [μm]: 0.50 ECCP-30CF₃ 4.50% Δn [589 nm, 20° C.:] 0.0954 ECCP-50CF₃ 4.50% Δε [kHz, 20° C.]: 5.7 CBC-33F 1.80% γ₁ [mPa · s, 20° C.]: 150 CBC-53F 1.80% d · Δn [μm]: 0.50 CBC-55F 1.80% Twist [°]: 90 PCH-6F 7.20% PCH-7F 5.40% CCP-20CF₃ 7.20% CCP-30CF₃ 10.80% CCP-40CF₃ 6.30% CCP-50CF₃ 9.90% PCH-5F 9.00% CWCZU-5-F 10.00% Example M2 CCP-2F.F.F 11.00% Clearing point [° C.]: 86.4 CCP-3F.F.F 10.00% Δn [589 nm, 20° C.:] 0.0802 CCP-30CF₃ 6.00% Δε [kHz, 20° C.]: 10.6 CGU-2-F 11.00% γ₁ [mPa · s, 20° C.]: 135 CGU-3-F 11.00% d · Δn [μm]: 0.50 CGU-5-F 9.00% Twist [°]: 90 BCH-3F.F.F 3.00% CCZU-3-F 15.00% CWCZU-3-F 11.00% CWCZG-3-F 10.00% CWCZP-3-OT 3.00% Example M3 CCP-2F.F.F 11.00% Clearing point [° C.]: 81.6 CCP-3F.F.F 10.00% Δn [589 nm, 20° C.:] 0.0818 CCP-30CF₃ 6.00% Δε [kHz, 20° C.]: 10.7 CGU-2-F 11.00% γ₁ [mPa · s, 20° C.]: 133 CGU-3-F 11.00% d · Δn [μm]: 0.50 CGU-5-F 10.00% Twist [°]: 90 BCH-3F.F.F 5.00% CCZU-3-F 15.00% CWCZU-3-F 11.00% CWCZG-3-OT 10.00% Example M4 PCH-7F 2.00% Clearing point [° C.]: 82.5 CCP-30CF₃ 8.00% Δn [589 nm, 20° C.]: 0.0831 CCP-20CF₃.F 10.00% Δε [kHz, 20° C.]: 9.6 CCP-30CF₃.F 9.00% γ₁ [mPa · s, 20° C.]: 161 CCP-50CF₃.F 12.00% d · Δn [μm]: 0.50 CCP-2F.F.F 12.00% Twist [°]: 90 CCP-3F.F.F 12.00% CCP-5F.F.F 6.00% CGU-2-F 5.00% CGU-3-F 6.00% CGU-5-F 9.00% CBC-33F 1.00% CWCZU-3-F 5.00% CWCZG-3-OT 3.00% Example M5 CCP-2F.F.F 12.00% Clearing point [° C.]: 96.6 CCP-3F.F.F 10.00% Δn [589 nm, 20° C.:] 0.0908 CCP-30CF₃.F 6.00% Δε [kHz, 20° C.]: 10.1 CCP-20CF₃ 6.00% γ₁ [mPa · s, 20° C.]: 162 CCP-30CF₃ 9.00% d · Δn [μm]: 0.50 CCP-50CF₃ 4.00% Twist [°]: 90 BCH-3F.F.F 17.00% BCH-5F.F.F 10.00% CCZU-3-F 15.00% CWCZU-3-F 6.00% CWCZG-3-OT 5.00% Example M6 CCP-2F.F.F 12.00% Clearing point [° C.]: 91.1 CCP-3F.F.F 12.00% Δn [589 nm, 20° C.:] 0.0825 CCP-30CF₃.F 3.00% Δε [kHz, 20° C.]: 10.2 CCP-20CF₃ 6.00% γ₁ [mPa · s, 20° C.]: 151 CCP-30CF₃ 8.00% d · Δn [μm]: 0.50 CCP-50CF₃ 7.00% Twist [°]: 90 CGU-2-F 9.00% CGU-3-F 8.00% CGU-5-F 5.00% CCZU-3-F 15.00% CWCZU-3-F 6.00% CWCZG-3-OT 6.00% CWCZP-3-OT 2.00% CC-3-V1 1.00% Example M7 PCH-5F 3.20% Clearing point [° C.]: 135.2 CCP-20CF₂.F.F 17.04% CCP-30CF₂.F.F 16.00% CCP-50CF₂.F.F 17.04% CUP-2F.F 5.36% CUP-3F.F 5.36% CBC-33F 5.36% CBC-53F 5.36% CBC-55F 5.28% CWCZU-5-F 20.02% Example M8 CCH-301 11.21% Clearing point [° C.]: 96.8 CCH-501 8.80% CCP-2F.F.F 8.00% CCP-3F.F.F 10.41% CCP-5F.F.F 4.00% CCZU-2-F 4.00% CCZU-3-F 13.61% CCZU-5-F 4.00% CH-33 2.40% CH-35 2.40% CH-43 2.40% CCPC-33 2.40% CCH-3CF₃ 6.40% CWCZU-5-F 19.96% Example M9 CCH-301 7.40% Clearing point [° C.]: 121.8 CCH-3CF₃ 4.23% Δn [589 nm, 20° C.:] 0.0693 CCH-501 5.82% CCP-2F.F.F 5.29% CCP-3F.F.F 6.87% CCP-5F.F.F 2.64% CCPC-33 1.59% CCZU-2-F 2.64% CCZU-3-F 8.99% CCZU-5-F 2.64% CH-33 1.59% CH-35 1.59% CH-43 1.59% CWCZU-5-F 47.12% Example M10 BCH-3F.F 10.80% Δn [589 nm, 20° C.:] +0.0954 BCH-5F.F 9.00% Δε [kHz, 20° C.]: +5.7 ECCP-30CF₃ 4.50% ECCP-50CF₃ 4.50% CBC-33F 1.80% CBC-53F 1.80% CBC-55F 1.80% PCH-6F 7.20% PCH-7F 5.40% CCP-20CF₃ 7.20% CCP-30CF₃ 10.80% CCP-40CF₃ 6.30% CCP-50CF₃ 9.90% PCH-5F 9.00% CWCZU-5F 10.00% Example M11 CCH-301 11.21% Clearing point [° C.]: +96.8 CCH-3CF₃ 6.40% Δε [kHz, 20° C.]: +7.3 CCH-501 8.80% CCP-2F.F.F 8.00% CCP-3F.F.F 10.41% CCP-5F.F.F 4.00% CCPC-33 2.40% CCZU-2-F 4.00% CCZU-3-F 13.61% CCZU-5-F 4.00% CH-33 2.40% CH-35 2.40% CH-43 2.40% CWCZU-5-F 19.96% Example M12 CCP-2F.F.F 11.00% CCP-3F.F.F 13.00% CCP-5F.F.F 6.00% CCZU-2-F 4.00% CCZU-3-F 16.00% CCZU-5-F 4.00% CGU-2-F 6.00% CGU-3-F 6.00% CCH-3CF₃ 4.00% CCOC-4-3 2.00% CWCZU-5-F 28.00% Example M13 CCH-301 23.00% CCZU-2-F 5.00% CCZU-3-F 19.00% CCZU-5-F 5.00% CCPC-33 3.00% CCPC-34 3.00% CCPC-35 2.00% CCOC-3-3 3.00% CCOC-4-3 4.00% CCOC-3-5 3.00% CH-33 3.00% CH-35 2.00% CH-43 2.00% CWCZU-5-F 23.00%

[0165] The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.

[0166] From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention and, without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions. 

1. A liquid-crystalline compound of formula I,

wherein R¹ is a straight-chain or branched alkyl radical having 1 to 15 C atoms which is unsubstituted, singly substituted by CN or CF₃, at least singly substituted by halogen, wherein optionally one or more CH₂ groups are substituted by —O—, —CO—, —S—, —CH═CH—, —C≡C—, —OC—O— or —O—CO— in such a way that O atoms are not directly linked together, R² is CN, SF₅, H, F, Cl, NCS, SCN or a straight-chain or branched alkyl radical having 1 to 15 C atoms which is unsubstituted, singly substituted by CN or CF₃, at least singly substituted by halogen, wherein optionally one or more CH₂ groups are substituted by —O—, —CO—, —S—, —CH═CH—, —C≡C—, —OC—O— or —O—CO— in such a way that O atoms are not directly linked together, A¹, A², A³ and A⁴ are each, independently, a 1,4-cyclohexenylene radical in which one or two non-adjacent CH₂ groups are optionally replaced by —O— or —S—, a 1,4-phenylene radical in which one or two CH groups are optionally replaced by N, or a radical selected from the group consisting of piperidine-1,4-diyl, 1,4-bicyclo[2.2.2]octylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, and 1,2,3,4-tetra-hydronaphthalene-2,6-diyl, wherein each is optionally singly substituted or polysubstituted by halogen, Z¹ and Z² are each, independently, —CO—O—, —O—CO—, —CF₂O—, —OCF₂—, —CH₂O—, —OCH₂—, —CH₂CH₂—, —(CH₂)₄—, —C₂F₄—, —CF₂CH₂—, —CH₂CF₂—, —CF═CF—, —CH≡CH—, —C≡C— or a single bond, a is 0, 1 or 2, b is 0, 1 or 2, and c is 0, 1 or 2, wherein a+b+c<2.
 2. A liquid-crystalline compound according to claim 1, wherein R¹ is a straight-chain alkyl radical of 1 to 10 C atoms or an alkenyl radical of 2 to 10 C atoms.
 3. A liquid-crystalline compound according to claim 1, wherein R¹ and R² are, each independently, a straight-chain alkyl or alkoxy radical of 2 to 7 C atoms.
 4. A liquid-crystalline compound according to claim 1, wherein R² is H, F, Cl, CN, CF₃, SF₅, CF₂H, OCF₃, OCF₂H, OCFHCF₃, OCFHCFH₂, OCFHCF₂H, OCF₂CH₃, OCF₂CFH₂, OCF₂CF₂H, OCF₂CF₂CF₂H, OCF₂CF₂CFH₂, OCFHCF₂CF₃, OCFHCF₂CF₂H, OCF₂CF₂CF₃, OCF₂CHFCF₃, or OCClFCF₂CF₃.
 5. A liquid-crystalline compound according to claim 1, wherein R² is F, CN, OCF₃, OCHF₂, CF₃, OCHFCF₃, OC₂F₅, OCF₂CHFCF₃, or a straight-chain alkyl or alkoxy.
 6. A liquid-crystalline compound according to claim 1, wherein c is
 0. 7. A liquid-crystalline compound according to claim 1, wherein a is 0
 8. A liquid-crystalline compound according to claim 1, wherein Z¹ and Z² are, each independently, a single bond, —CF₂O—, —OCF₂—, —C₂F₄ ⁻, —CH₂O—, —OCH₂—, or —COO—.
 9. A liquid-crystalline compound according to claim 1, which is of the formulae I1 to I24,

wherein R¹ is a straight-chain or branched alkyl radical having 1 to 15 C atom which is unsubstituted, singly substituted by CN or CF₃, at least singly substituted by halogen, wherein optionally one or more CH₂ groups are substituted by —O—, —CO—, —S—, —CH═CH—, —C≡C—, —OC—O— or —O—CO— in such a way that O atoms are not directly linked together, and alkyl is a straight-chain or branched alkyl radical of 1-9 C atoms.
 10. A liquid-crystalline medium, comprising at least one compound of formula I of claim 1 and at least one additional mesogenic compound.
 11. A liquid-crystalline medium according to claim 10, further comprising one or more compounds of formulae II, III, IV, V, VI, VII, VIII, IX or X,

wherein R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 C atoms, X⁰ is halogenated alkyl, halogenated alkenyl, halogenated alkenyloxy, halogenated alkoxy, each having up to 7 C atoms, F or Cl, Z⁰ is —CH═CH—, —C₂H₄—, —C₂F₄—, —CF═CF—, —CF₂O—, —OCF₂— or —COO—, Y¹, Y², Y³ and Y⁴ are, each independently, H or F, and r is 0 or
 1. 12. A liquid-crystalline medium according to claim 11, comprising at least 50 wt % of compounds of formulae I to X.
 13. A liquid-crystalline medium according to claim 10, comprising 5 to 50 wt % at least one compound of formula I.
 14. A liquid-crystalline medium according to claim 10, further comprising one or more compounds of formulae RI to RX,

wherein R⁰ is n-alkyl, oxaalkyl, fluoroalkyl, alkenyloxy or alkenyl, each having up to 9 C atoms, d is 0, 1 or 2, Y¹ is H or F, Alkyl or Alkyl* is, each independently, a straight-chain or branched alkyl radical having 1-9 C atoms, and Alkenyl or Alkenyl* is, each independently, a straight-chain or branched alkenyl radical having up to 9 C atoms.
 15. A liquid-crystalline medium according to claim 11, wherein X⁰ is F, OCHF₂ or OCF₃.
 16. In an electro-optical liquid-crystal display comprising a liquid-crystalline medium, the improvement wherein said medium contains a compound according to claim
 1. 17. In a method of generating, an electro-optical effect using a liquid-crystal display, the improvement wherein said display is in accordance with claim
 16. 